PRO-VAC MLR-5
REINFORCED TEFLON MOULD RELEASE
High quality self-adhesive Teflon coated glass mould release for composite processing applications.
Adheres to composite and metal tools as well as wooden moulds and plugs.
The adhesive system is pressure sensitive therefore is stable throughout vacuum and autoclave curing.
Recommended for use on flat or single curvature surfaces, can be joined using a butt joint.
Technical data
| Part number | PRO-VAC MLR-5 | PRO-VAC MLR-3 |
|---|---|---|
| Reinforcement | Woven glass | Woven glass |
| Coating | PTFE | PTFE |
| PTFE content | 55% | 67% |
| Adhesive | Silicone | Silicone |
| Nominal coated fabric thickness | 0,116 mm | 0.07 mm |
| Adhesive weight | 55 g/m2 | 50 g/m2 |
| Peel Adhesion | 12 N/ 2.5cm | 12 N/ 2.5cm |
| Max use temperature | 260°C | 260°C |
| Width | 1000 mm | 1000 mm |
Packaging and storage
Store in original packing at room temperature (22 °C).
Shelf life of 8 months from date of manufacture.